LKT0603X0R5M250R [KINGTRONICS]
Low Voltage Multilayer Chip Ceramic Capacitor; 低压多层片式陶瓷电容器型号: | LKT0603X0R5M250R |
厂家: | Kingtronics International Company |
描述: | Low Voltage Multilayer Chip Ceramic Capacitor |
文件: | 总8页 (文件大小:365K) |
中文: | 中文翻译 | 下载: | 下载PDF数据表文档文件 |
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
Capacitance and Capacitance Tolerance
Different circuit needs different capacitance and capacitance tolerance. So the selection of capacitance is depended on the need of
customers.
■ Dielectric Material Type of Capacitor
-NPO : The capacitor of this kind dielectric material is considered as ClassⅠcapacitor, including general capacitor and high frequency
NPO capacitor. The electrical properties of NPO capacitor are the most stable one and have little change with temperature, voltage and
time. They are suited for applications where low-losses and high-stability are required, such as filters, oscillators, and timing circuits.
- X7R, X5R : X7R, X5R material is a kind of material has high dielectric constant. The capacitor made of this kind material is considered
as Class Ⅱcapacitor whose capacitance is higher than that of class Ⅰ. These capacitors are classified as having a semi-stable temperature
characteristic and used over a wide temperature range, such in these kinds of circuits, DC-blocking, decoupling, bypassing, frequency
discriminating etc.
-Y5V : The capacitor made of this kind of material is the highest dielectric constant of all ceramic capacitors. They are used over a
moderate temperature range in application where high capacitance is required because of its unstable temperature coefficient, but where
moderate losses and capacitance changes can be tolerated. Its capacitance and dissipation factors are sensible to measuring conditions,
such as temperature and voltage, etc.
Temperature Range
NPO/ X7R: -55~125℃
X5R: -55~85℃
Y5V: -30~85℃
Voltage
16, 25, 50, 63 VDC.
Capacitance
0.5pF ~ 10uF
Terminations
Tin / Nickel
Tolerance
±0.1pF , +80 ~ -20%
Packing
Tape and Reel (0402, 0603, 0805, 1206, 1210, 1812, 2220)
Dielectric & Values
NPO X7R Y5V Z5U consult product pages of catalog for cap ranges and voltage rating
1
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
How To Order
LKT
|
0805
N
|
102
J
|
500
R
|
|
|
|
Series
1.
2.
3.
4.
5.
6
NOTE:
1. Dimensions
Size Code
LxW (inch)
0402
0.04x0.02
0603
0.06x0.03
0805
1206
0.12x0.06
0.08x0.05
2. Dielectric Style
Dielectric Code
N
B
X
F
Dielectric material
NPO
X7R
X5R
Y5V
3. Nominal Capacitance
Unit : pF
102
0R5
1R0
224
…
10X102
0.5
1.0
22X104
…
Note : First two digits are significant; third digit denotes number of zeros; R = decimal.
4. Capacitance Tolerance
Code
C
D
J
K
M
Z
+80%
-20%
Tolerance
±0.25pF
±0.5pF
±5.0%
±10%
±20%
5. Rated Voltage
Express
160
Method
250
500
Actual
16V0
25V0
50V0
Value
6. Pb
Code
Pb
R
RoHS
2
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
Specification and Test Condition:
1. Appearance
Dielectrics
Specification
Testing Condition
Visual inspection
NPO/X7R/X5R/Y5V
No defects or abnormalities
2. Dimensions
Dielectrics
Specification
Testing Condition
NPO/X7R/X5R/Y5V
Within the specified dimensions
Using calipers on micrometer
3. Capacitance
Dielectrics
Specification
Testing Condition
1.0±0.2Vrms, 1MHz±10%
(C>1000 pF, 1.0±0.2Vrms, 1KHz±10%,)
25℃
Within the specified tolerance
B:±0.1pF;C:±0.25pF;D:±0.5pF;J: ±5%
NPO
1.0±0.2Vrms, 1KHz±10%
(Cp>10uF,0.5±0.1Vrms,120±24Hz)
at 25℃,48hrs after annealing
Within the specified tolerance
J: ±5%;K: ±10%; M: ±20%
X7R/X5R
1.0±0.2Vrms, 1KHz±10%
(Cp>10uF,0.5±0.1Vrms,120±24Hz)
at 25℃, 48hrs after annealing
Within the specified tolerance
M: ±20%; Z: +80% ~ -20%
Y5V
4. Dissipation Factor
Dielectrics
Specification
Testing Condition
Cp<30pF, Q≥400+20Cp;
Cp≥30pF, Q≥1000
1.0±0.2Vrms,1MHz±10% ,25℃
(Cp>1000pF,1.0±0.2Vrms,1KHz±10%)
1.0±0.2Vrms, 1KHz±10%,
(Cp>10uF,0.5±0.1Vrms,120±24Hz)
at 25℃,48hrs after annealing
NPO
VR≥25V, DF ≤2.5%
VR =16V, DF ≤3.5%
VR ≤10V, DF ≤5.0%
VR≥25V, DF ≤7.0% (C<1.0μF)
DF ≤9.0% (C≥1.0μF)
VR =16V, DF ≤9.0%
VR ≤10V, DF ≤12.5%
X7R/X5R
1.0±0.2Vrms, 1KHz±10%,
(Cp>10uF,0.5±0.1Vrms,120±24Hz)
at 25℃,48hrs after annealing
Y5V
5. Insulation Resistance
Dielectrics
Specification
Testing Condition
NPO/X7R/
X5R/Y5V
More than 10 GΩ or 500Ω·F, whichever is
smaller.
Rated voltage for 60±5sec, at 25℃
6. Dielectric Strength
Dielectrics
Specification
Testing Condition
No failure shall be observed when 300% (NPO);250%
(X7R/ X5R/Y5V)of the rated voltage is applied between
terminations for 1 to 5 seconds, provided the charge
/discharge current is less than 500mA
NPO /X7R/X5R/Y5V
No defects or abnormalities.
3
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
7. Temperature Coefficient of Capacitance
Dielectrics
Specification
Testing Condition
Measure capacitance under follow table list temperature:
Temperature coefficient within ±30ppm/℃
Cp drift within ±0.2% or ±0.05pF
STEP
1
2
3
4
5
NPO, X7R
25 ±2
-55±3
25 ±2
125±3
25 ±2
X5R
Y5V
NPO
25 ±2
-55±3
25 ±2
85±3
25 ±2
25 ±2
-30±3
25 ±2
85±3
25 ±2
X7R/X5R
Capacitance change within ±15%
1) NPO
The capacitance drift is calculated by dividing the
differences between the maximum and minimum measured
values in the step 1,3 and 5.
The temperature coefficient is determined using the
Capacitance measured in step 3 as a reference.
2) X7R ,X5R and Y5V
Y5V
Capacitance change within +22%, -82%
The ranges of capacitance change compared within the
above 25℃ value over the temperature ranges shall be
within the specified ranges.
8. Adhesion
Dielectrics
Specification
Testing Condition
The pressurizing force shall be 10N (=1000g*f) and the
duration of application shall be 10±1sec.
hooked jig
NPO
X7R/X5R
Y5V
No removal of the terminations or other
defect shall occur.
board
r=0.5
hip
cross-section
9. Solderability of Termination
Dielectrics
Specification
Testing Condition
NPO
95% min. coverage of both terminal Solder temperature: 230±5℃
X7R/X5R
Y5V
electrodes and less than 5% have pin holes Dipping time: 2±1 seconds.
or rough spots.
Completely soak both terminal electrodes in solder
10. Resistance to leaching
Dielectrics
Specification
Testing Condition
95% min. coverage of both terminal
electrodes and less than 5% have pin holes
or rough spots.
NPO
X7R/X5R
Y5V
Solder temperature: 270±5℃
Dipping time: 10±1 seconds.
Completely soak both terminal electrodes in solder
No remarkable visual damage.
4
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
11. Bending
Dielectrics
Specification
Testing Condition
Solder the capacitor on testing substrate and put it on
testing stand. The middle part of substrate shall
successively be pressurized by pressuring rod at a rated of
about 1.0mm/sec. Until the deflection become means of the
1.0mm.
No remarkable visual damage
Cp change ≤ ±5% or ≤ 0.5 pF
NPO
No remarkable visual damage
Cp change ≤ ±12.5%
X7R/X5R
No remarkable visual damage
Cp change ≤ ±30%
Y5V
12. Resistance to Soldering Heat
Dielectrics
Specification
Testing Condition
No remarkable visual damage
Cp change within ±2.5% or ±0.25pF,
whichever is larger.
DF meets initial standard value.
IR meets initial standard value.
No remarkable visual damage
Soldering temperature: 270±5℃
Preheating: 120~150℃ 60sec.
Dipping time: 10±1 seconds.
NPO
Measurement to be made after being kept at room
temperature for 24±2 (COG) or 48±4(X7R ,X5R, Y5V)
hours.
Recovery for the following period under the standard
condition after test.
*Initial measurement for high dielectric constant type
Perform a heat treatment at 140~150℃ for 1hr and let sit
for 48±4hrs at room temperature. Perform the initial
measurement.
Cp change within ±5%
X7R/X5R
Y5V
DF meets initial standard value.
IR meets initial standard value.
No remarkable visual damage
Cp change within ±20%
DF meets initial standard value.
IR meets initial standard value.
13. Temperature Cycle
Dielectrics
Specification
Testing Condition
To perform 5 cycles of the stated environment:
Step
Temperature
Min. operating Temp.+0/-3℃
25℃
Max. operating Temp.+0/-3℃
25℃
Time
30min
2~3 min
30 min
2~3 min
No remarkable visual damage
Cp change within ±2.5% or ±0.25pF,
whichever is larger.
NPO
1
2
3
4
Measurement to be made after being kept at room
temperature for 24±2hrs (COG) or 48±4hrs (X7R, X5R,
Y5V) at room temperature, then measure.
*Initial measurement for high dielectric constant type
Perform a heat treatment at 140~150℃ for 1hr and let sit
for 48±4hrs at room temperature.
No remarkable visual damage
Cp change within ±7.5%
X7R/X5R
Perform the initial measurement.
5
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
14. Moisture Resistance ,steady state
Dielectrics
Specification
Testing Condition
No remarkable visual damage
Cp change within ±5% or ±0.5pF,
whichever is larger.
Cp<10pF, Q≥200+10Cp;
IO≤Cp<30pF, Q≥275+2.5Cp
Cp≥30pF, Q≥350
R*C≥1000MΩ or 50Ω·F, whichever is
smaller
Cp change within ±12.5%
DF: Not more than 2 times of initial value
R*C≥1000MΩ or 50Ω·F, whichever is
smaller
No remarkable visual damage
Cp change within ±30%
DF: Not more than 1.5 times of
initial value
R*C≥1000MΩ or 50Ω·F, whichever is
smaller
Test temperature: 40±2℃
Humidity: 90~95% RH
Testing time: 500 ±12hrs
NPO
Measurement to be made after being kept at room
temperature for 24±2hrs (COG) or 48±4hrs (X7R, X5R,
Y5V)
X7R/X5R
Y5V
*Initial measurement for high dielectric constant type
Perform a heat treatment at 140~150℃ for 1hr and let sit
for 48±4hrs at room temperature.
Perform the initial measurement.
15. Damp heat with load
Dielectrics
Specification
Testing Condition
No remarkable visual damage
Cp change≤±7.5% or ±0.75pF, whichever
is larger.
NPO
Cp<30pF, Q≥100+10/3*Cp
Cp≥30pF, Q≥200
Test temperature: 40±2℃
Humidity: 90~95% RH
Voltage: 100% of the rated voltage
Testing time: 500 ±12hrs
R*C≥500MΩ or 25Ω·F, whichever is
smaller
No remarkable visual damage
Cp change≤±12.5%
DF: Not more than 2 times of initial value
R*C≥500MΩ or 25Ω·F, whichever is
smaller
No remarkable visual damage
Cp change≤±30%
DF: Not more than 1.5 times of
initial value
R*C≥500MΩ or 25Ω·F , whichever is
smaller
Measurement to be made after being kept at room
temperature for 24±2hrs (COG) or 48±4hrs (X7R, X5R,
Y5V)
X7R/X5R
Y5V
*Apply the rated DC voltage for 1 hour at 40±2℃.
Remove and let sit for 48±4hrs at room temperature.
Perform the initial measurement.
16. Life Test
Dielectrics
Specification
Testing Condition
No remarkable visual damage
Cp change≤±3% or ±0.3pF, whichever is
larger.
Q≥350 (Cp≥30 PF)
Q≥275+(2.5* Cp) (10 pF≤Cp<30 PF)
Q≥200+10*Cp (Cp<10 PF)
R*C≥1000MΩ or 50Ω·F, whichever is smaller
No remarkable visual damage
Cp change≤±12.5%
DF:Not more than 2 times of initial value
R*C≥1000MΩ or 50Ω·F, whichever is smaller
Test temperature:
Max. Operating Temp. ±3℃
Voltage:
200% of the rated voltage
Testing time: 1000 hrs
NPO
Measurement to be made after being kept at room temperature
for 24±2hrs (COG) or 48±4hrs (X7R, X5R,Y5V)
X7R/X5R
Y5V
*Initial measurement for high dielectric constant type
Apply 200% of the rated DC voltage for one hour at the
maximum operating temperature ±3℃.
Remove and let sit for 48±4hrs at room temperature.
Perform the initial measurement
No remarkable visual damage
Cp change≤±30%
DF:Not more than 1.5 times of
initial value
R*C≥1000MΩ or 50Ω·F, whichever is smaller
6
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
Packing
1. Tape Packing
Paper Tape: Standard taping (8mm paper width) suitable to 0603,0805,4Kpcs/reel
To 0402, 10Kpcs/reel.
Plastic Tape: Suitable 0805, 1206 sizes, for chip thickness over 0.95 mm, 4Kpcs/reel
or 3Kpcs/reel are available.
2. Dimensions of Packing Paper:
Type
0402
0603
0805
1206
A
B
C
D
T
0.65±0.10
1.05±0.10
1.55±0.15
1.95±0.15
1.15±0.10
1.85±0.10
2.3±0.15
3.5±0.15
2.0±0.05
4.0±0.10
4.0±0.10
4.0±0.10
2.0±0.05
2.0±0.10
2.0±0.10
2.0±0.10
0.8max
1.1max
1.1max
1.1max
3. Dimensions of Embossed Packing
A:1.45±0.20 B:2.25±0.20 (0805)
A:1.95±0.20 B:3.50±0.20 (1206)
7
Website: www.kingtronics.com
Email: info@kingtronics.com Tel: (852) 8106 7033 Fax: (852) 8106 7099
LKT
Low Voltage Multilayer Chip Ceramic
Capacitor
4. Dimensions of Reel:
φ180mmReel
5. Taping Figure
6. Taping Method
①Tapes for capacitors are wound clockwise. The sprocket holes are to the right as the tape is pulled toward the user.
②The top tape and base tape are not attached at the end of the tape for a minimum of 5 pitches.
③Part of the leader and part of the empty tape shall be attached to the end of the tape as follows.
④Missing capacitors number within 0.1% of the number per reel or 1pc, whichever is greater, and are not continuous.
⑤The top tape and bottom tape shall not protrude beyond the edges of the tape and shall not cover sprocket holes.
⑥Cumulative tolerance of sprocket holes, 10 pitches: ±0.3mm.
⑦Peeling off force: 0.1 to 0.6N in the direction shown down.
Note: Specifications are subject to change without notice.