CZP2BFLTE650P [KOA]
Ferrite Chip, 1 Function(s), 2A, EIA STD PACKAGE SIZE 1206, 2 PIN;型号: | CZP2BFLTE650P |
厂家: | KOA SPEER ELECTRONICS, INC. |
描述: | Ferrite Chip, 1 Function(s), 2A, EIA STD PACKAGE SIZE 1206, 2 PIN |
文件: | 总10页 (文件大小:196K) |
中文: | 中文翻译 | 下载: | 下载PDF数据表文档文件 |
KOA SPEER ELECTRONICS, INC.
SS-220 R11
AHA 11/29/04
CERTIFIED
Multi Layer Ferrite Power Beads
Type CZP
1. General
ꢀ
Designed to reduce noise at high frequencies
ꢀ
Standard EIA Packages: 1J, 2A, 2B
ꢀ
Nickel barrier with solder overcoat for excellent solderability
Magnetically shielded
ꢀ
2. Dimensions
Table 1
Dimensions - inches (mm)
W
L
Part
L
W
t
d
Solder
Plating
Ni
0.063 0.006
(1.60 0.15ꢀ
0.031 0.006
(0.80 0.15ꢀ
0.031 0.006
(0.80 0.15ꢀ
0.014 0.006
(0.36 0.15ꢀ
1J
(0603)
Plating
Silver
Metallization
t
d
0.079 0.008
(2.00 0.20ꢀ
0.049 0.008
(1.25 0.20ꢀ
0.035 0.008
(0.90 0.20ꢀ
0.020 0.010
(0.51 0.25ꢀ
2A
(0805)
Terminations
(Metallization
Bandsꢀ
d
Electrodes
0.126 0.008
(3.20 0.20ꢀ
0.063 0.008
(1.60 0.20ꢀ
0.043 0.008
(1.10 0.20ꢀ
0.020 0.010
(0.51 0.25ꢀ
2B
(1206)
3. Type Designation
The type designation shall be in the following form:
New Type
CZP
Type
2A
Size
F
T
TD
500
P
Termination
Material
Impedence
Tolerance
Packaging
Permability
Code
1J
2A
2B
F
P
T: Sn
L: SnPb
TE: 7" Embossed Plastic
1J, 2A: 4,000 pcs/reel
2B: 3,000 pcs/reel
2 significant
figures + 1
multiplier
P: 25ꢁ
PAGE 1 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
4. Standard Applications
Impedance
Maximum DC
Allowable
DC Current
(mA)
†
††
Ordering
Code
@ 100MHz
Resistance
Operating
Temperature
Ω
Ω
CZP1JF*TE050P
CZP1JF*TE300P
CZP1JF*TE600P
CZP1JF*TE121P
CZP1JF*TE181P
CZP1JF*TE301P
CZP2AF*TE070P
CZP2AF*TE100P
CZP2AF*TE110P
CZP2AF*TE150P
CZP2AF*TE220P
CZP2AF*TE300P
CZP2AF*TE400P
5
30
0.04
0.06
0.1
1,000
3,000
500
-55°C
to
60
120
180
300
7
0.1
2,000
1,500
2,000
3,000
3,000
3,000
3,000
3,000
3,000
2,000
125°C
0.15
0.1
0.02
0.02
0.025
0.025
0.025
0.015
0.03
10
11
15
22
30
40
-55°C
to
125°C
CZP2AF*TE450P
CZP2AF*TE600P
CZP2AF*TE800P
45
60
80
0.03
0.025
0.1
2,000
3,000
1,000
CZP2AF*TE201P
CZP2AF*TE221P
CZP2AF*TE301P
CZP2AF*TE601P
CZP2AF*TE102P
200
220
0.15
0.05
0.15
0.2
1,000
2,000
1,000
1,000
1,000
300
600
1000
0.2
CZP2BF*TE190P
CZP2BF*TE260P
CZP2BF*TE300P
CZP2BF*TE310P
CZP2BF*TE500P
CZP2BF*TE650P
CZP2BF*TE700P
CZP2BF*TE800P
19
26
30
31
50
65
70
80
0.02
0.02
0.02
0.02
0.025
0.03
0.03
0.03
3,000
3,000
3,000
3,000
3,000
2,000
2,000
-55°C
to
125°C
2,000
*Add Termination Material Character (L,Tꢀ
† Impedance Test Method: HP4291A
†† DCR Test Method: Keithley 580
PAGE 2 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
4. Standard Applications (continuedꢀ
Impedance
Maximum DC
Allowable
DC Current
(mA)
†
††
Ordering
Code
@ 100MHz
Resistance
Operating
Temperature
Ω
Ω
CZP2BF*TE900P
CZP2BF*TE101P
CZP2BF*TE121P
CZP2BP*TE700P
CZP2BF*TE601P
CZP2BP*TE101P
CZP2BP*TE121P
CZP2BP*TE601P
*Add Termination Material Character (L,Tꢀ
90
100
120
70
0.1
0.1
1,000
1,000
0.1
1,000
-55°C
to
125°C
0.2
3,000
600
100
120
600
0.2
1,000
3,000
0.03
0.04
0.1
3,000
1,500
† Impedance Test Method: HP4291A
†† DCR Test Method: Keithley 580
5. 0603 (1J) Graphs
CZP1JF050
CZP1JF100
CZP1JF300
CZP1JF301
CZP1JF600
PAGE 3 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
5. 0805 (2A) Graphs
CZP2AF100
CZP2AF070
CZP2AF100
CZP2AF201
CZP2AF150
CZP2AF110
CZP2AF221
CZP2AF301
CZP2AF300
CZP2AF601
CZP2AF400
CZP2AF450
PAGE 4 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
5. 0805 (2A) Graphs (continuedꢀ
CZP2AF800
5. 1206 (2B) Graphs
CZP2BF101
CZP2BF121
CZP2BF190
CZP2BF310
CZP2BF650
CZP2BF260
CZP2BF300
CZP2BF500
CZP2BF500
PAGE 5 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
5. 1206 (2B)Graphs (continuedꢀ
CZP2BF900
CZP2BF800
CZP2BF700
CZP2BP601
CZP2BP121
CZP2BP101
PAGE 6 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
5. Characteristics
Item
Requirement
Conditions
Operating Temperature
Storage Temperature
-55°C ~ +125°C
40°C @ 70ꢁ Humidity
Sealed plastic bags with desiccant shall be
used to reduce the potential of oxidation on
the terminations during storage.
Resistance to Solder
Heat
Change in Impedance: Relative to value before
test 20ꢁ.
Appearance: There shall be no cracking
Flux: 5-10 sec dip
After Flux: Air dry for 15 sec
Preheat: 150°C 10°C
Solder Coverage: More than 75ꢁ of the terminal Preheat Time: 60 sec
electrode shall be covered with solder.
Solder Temp: 260°C 5°C
Dip Time: 10 1 sec
Solderability
Solder Coverage: More than 95ꢁ of the
Flux: 5-10 sec dip
termination shall be covered with solder.
After Flux: Air dry for 15 sec
Solder Temp: 245°C 5°C
Dip Time: 5 0.5 sec
Leach Resistance
Appearance: There shall be no visible signs of
physical or mechanical damage (i.e. no cracksꢀ.
Terminations: Termination must not be leached
away for more than 5ꢁ.
The bead shall be subjected to the following
5 steps for the period of time shown below.
The 5 steps constitute one (1ꢀ rotation.
4 rotations shall be carried out.
1) Flux: 5-10 sec
2) After Flux: Air dry for 15 sec
3) Solder Temp: 230°C 5°C
4) Dip Time: 5 0.5 sec
5) Cool: Air cool for 60 seconds
Insulation Resistance
Solvent Resistance
Insulation Resistance: Min 1G ohms
Change in Impedance: Relative to value before
Cleaning by:
test 10ꢁ.
Washer: Ultrasonic washer (100Wꢀ
Solvent: Isopropyl alcohol
Time: 3 minutes
Terminal Strength
(hanging testꢀ
Appearance: The terminal electrode shall not
break off, nor shall there be damage to the body.
Type
1J
2A
W(kgf)
0.5
1.0
Time
30 sec 2 sec
30 sec 2 sec
30 sec 2 sec
2B
1.5
Terminal Strength
(push testꢀ
Appearance: There shall be no evidence of
mechanical degradations to terminals or body.
Type
1J
2A
W(kgf)
1.4
1.8
Time
60 sec
60 sec
60 sec
2B
2.3
Bending Strength
Appearance: There shall be no physical or
mechanical damage.
Board: 90x40x1.6mm
Bend: 1mm
Impedance: Relative to initial value before test
Time: 5 sec
10ꢁ.
PAGE 7 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
5. Characteristics (continuedꢀ
Item
Requirement
Conditions
Mechanical Shock
Appearance: There shall be no physical or
mechanical damage.
Force: 50G
Time: 11 msec
Impedance: Relative to initial value before test
10ꢁ.
There shall be 3 shocks in each of 6 directions
(18 shocks totalꢀ.
Vibration
Impedance: Relative to initial value 10ꢁ.
Only endurance conditioning by sweeping shall
be made. The entire frequency range from
10-2,000Hz and return to 10Hz in 20
minutes (this shall constitute one cycleꢀ.
Amplitude: 1.5mm
The test shall have a 15G peak and shall be
applied for a period of 4 hours (12 cyclesꢀ
in each of 3 mutually perpendicular directions
(a total of 36 cycles within a total of 12 hoursꢀ.
Thermal Shock
Appearance: There shall be no physical or
mechanical damage.
Step
1-start
Temperature
-40°C 2°C
Time
Impedance: Relative to initial value 20ꢁ.
DCR: The DCR shall not exceed initial specified
value.
2-hold
3-transfer
4-hold
-40°C 2°C 30 min 5 min
0.5 min max.
+105°C 2°C 30 min 5 min
0.5 min max.
5-transfer
Testing of the parts will be made at 0 hours, 250
hours and 500 hours. Before testing, the parts
shall be allowed to cool to room temperature for
24 hours.
Steps 1 thru 5 constitute one complete cycle
and the test shall consist of a total of 500
cycles.
Load Humidity
Appearance: There shall be no physical or
mechanical damage.
Impedance: Relative to initial value 15ꢁ.
Temperature: 85°C 2°C
Relative Humidity: 85ꢁ
Time: 1,000 hours total
Apply: 100ꢁ rated current
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
Life Test
Appearance: There shall be no physical or
mechanical damage
Impedance: Relative to initial value 15ꢁ
Temperature: 85°C 2°C
Time: 1,000 hours total
Apply: 100ꢁ rated current
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
PAGE 8 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
6. Packaging Specifications
KOA’s multilayer components are provided on tape-and-reel for use in pick-and-place machines.
The reel size is 7 inch.
7. Dimensions - inches (mm)
+0.1
1.5
-0
B
T1
T1
Direction of feed
T1
2.0 4.0–0.1
P1
Dimensions - inches (mm)
Tape
A
B
W
P1
T1
1J
0603
0.075 0.002
(1.9 0.1)
0.043 0.002
(1.1 0.1)
0.318 0.002
(8.1 0.1)
0.157 0.004
(4.0 0.1)
0.043 0.002
(1.1 0.1)
2A
0805
0.093 0.002
(2.4 0.1)
0.063 0.002
(1.6 0.1)
0.318 0.002
(8.1 0.1)
0.157 0.004
(4.0 0.1)
0.046 0.002
(1.2 0.1)
2B
1206
0.138 0.002
(3.5 0.1)
0.071 0.002
(1.8 0.1)
0.318 0.002
(8.1 0.1)
0.157 0.004
(4.0 0.1)
0.071 0.002
(1.8 0.1)
Dimensions - inches (mm)
(mm)
Tape
øa
ød
e
Central hole
1J
0603
2A
0805
7
0.827
(21)
0.079
(2.0)
(178)
¿13
¿d
2B
1206
e
PAGE 9 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-220 R11
9. Recommended PC Board Land Patterns - mm (inches)
Chip Size
1J (0603)
2A (0805)
2B (1206)
L
G
H
2.6 (0.102)
3.0 (0.118)
4.4 (0.173)
0.6 (0.023)
1.0 (0.039)
2.2 (0.087)
0.8 (0.031)
1.0 (0.039)
1.4 (0.055)
H
G
L
10. Recommended Temperature Profiles for Soldering
Recommended Temperature Profile
for Wave Soldering
Recommended Temperature Profile
for Reflow Soldering
Preheat 100
Seconds Max.
Soldering
10 Seconds Max.
Natural
Cooling
Preheat 100
Seconds Max.
Soldering
10 Seconds Max.
Natural
Cooling
250°C
150°C
250°C
150°C
200°C
20 Seconds Max.
60 Seconds Max.
60 Seconds Max.
PAGE 10 OF 10
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
ꢀ
Bolivar Drive
P.O. Box 547
Bradford, PA 16701
USA
814-362-5536
Fax 814-362-8883
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.