225506015637 [YAGEO]

Ceramic Capacitor, Multilayer, Ceramic, 50V, 10% +Tol, 10% -Tol, X7R, 15% TC, 0.012uF, Surface Mount, 1206, CHIP;


型号：	225506015637
厂家：	YAGEO CORPORATION
描述：	Ceramic Capacitor, Multilayer, Ceramic, 50V, 10% +Tol, 10% -Tol, X7R, 15% TC, 0.012uF, Surface Mount, 1206, CHIP
文件：	总9页 (文件大小：177K)
中文：	中文翻译
下载：	下载PDF数据表文档文件

DATA SHEET

SURFACE-MOUNT CERAMIC

MULTILAYER CAPACITORS

Low-inductance: Class 2, X7R

10/16/25/50 V

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

FEATURES

QUICK REFERENCE DATA

VALUE

• Three standard sizes

DESCRIPTION

• For high frequency applications

• Supplied in tape on reel

• NiSn terminations.

0306

0508

0612

Rated voltage U_r(DC)

10 V

16 V; 25 V

50 V

Capacitance range /E6 series, (nF);

note 1:

10 V

16 V

25 V

50 V

100 to 220

−

APPLICATIONS

−

100 to 220

10 to 100

−

Consumer electronics, for example:

• High speed IC packages

10 to 100

• Processor package decoupling

Tolerance on cap. after 1,000 hours ±10%, ±20%; note 2

• AC noise reduction in multi-chip

2.5 × U_r

Test voltage (DC) for 1 min.

modules.

Equivalent series inductance

10 V

300 pH

−

DESCRIPTION

16 V

−

600 pH

−

25 V

−

The capacitor consists of a

rectangular block of ceramic

dielectric in which a number of

interleaved metal electrodes are

contained. This structure gives rise

to a high capacitance per unit

volume.

50 V

500 pH

Sectional specifications

IEC 60384-10, second edition 1989-

04; also based on CECC 32 100

Detailed specification

End terminations

based on CECC 32 101-801

NiSn

Climatic category (IEC 60068)

55/125/56

The inner electrodes are connected

to the two terminations and finally

covered with a layer of plated tin

(NiSn). A cross section of the

structure is shown in Fig.1.

Notes

1. Other values on request.

2. Special tolerance values available on request.

terminations

electrodes

MLB457

ceramic material

Fig.1 Construction of a ceramic multilayer capacitor.

2004 May 14 Rev.8

www.yageo.com

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

MECHANICAL DATA

CCB397

For dimensions see Table 1.

Fig.2. Component outline.

Physical dimensions

Table 1 Capacitor dimensions in mm; see Fig.2

L₂AND L₃

L₄

MIN

L₁

CASE SIZE

MIN.

0.10

0.13

MAX.

0.30

0.46

0306

0508

0612

0.8 ±0.15

1.25 ±0.20

1.60 ±0.20

2.00 ±0.20

3.20 ±0.20

0.50 ±0.10

0.85 ±0.10

0.2

0.38

0.50

Footprint

Table 2 Footprint dimensions; see Fig.3

FOOTPRINT DIMENSIONS

CASE

SIZE

(mm)

0306

0508

0612

0.4

1.6

0.45

0.50

0.760

2.00

3.05

0.73

0.89

CCB408

For dimensions see Table 2.

Fig.3 Footprint dimensions.

2004 May 14 Rev.8

www.yageo.com

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

SELECTION CHART

LAST TWO

DIGITS OF

10 V

0306

16 V

0508

25 V

50 V

0612

(nF)

12NC

0.85 ±0.10

100

120

150

180

220

0.50 ±0.10

0.85 ±0.10

Thickness classification and packing quantities

8 mm TAPE WIDTH

QUANTITY PER REEL

THICKNESS

CLASSIFICATION

∅180 mm; 7"

(mm)

∅330 mm; 13"

PAPER

BLISTER

PAPER

BLISTER

0.85 ±0.10

4000

15000

2004 May 14 Rev.8

www.yageo.com

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

ORDERING INFORMATION

Components may be ordered by using either Phycomp’s unique 12NC or a simple 15-digit clear text code.

Ordering code 12NC (preferred)

2 2 X X X X X X 5 X X X

(1)

Carrier type

Capacitance value

55 paper tape

Rated voltage - Termination

Tolerance

06 50 V; Ni-barrier

07 25 V; Ni-barrier

08 16 V; Ni-barrier

09 10 V; Ni-barrier

10%

20%

(2)

Packaging

Size

reel: ∅180 mm; 7"

reel: ∅330 mm; 13"

0306 low inductance

0612 low inductance

0508 low inductance

SCM033

(1) Refer to chapter “Selection chart”

(2) Quantity on reel depends on thickness classification, see section “Thickness classification and packing quantities”.

Clear text code

EXAMPLE: 12062E104M9B20D

Size

Code

Temp.

Char.

Capacitance

Tol.

Vol.

Termination

Packing

Marking

Series

0306 2R = X7R 103 = 10,000

K = ±10% 6 = 10 V B = NiSn

2 = 180 mm;

7" paper

3 = 330 mm;

13" paper

0 = no marking L = low

inductance

pF; the third

digit signifies

7 = 16 V

0508

M= ±20%

8 = 25 V

9 = 50 V

0612

the multiplying

factor:

3 = × 1,000

4 = × 10,000

2004 May 14 Rev.8

www.yageo.com

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

ELECTRICAL DATA

Class 2 capacitors; low inductance; NiSn terminations

Unless otherwise stated all electrical values apply at an ambient temperature of 20 ±1 °C, an atmospheric pressure of

86 to 105 kPa, and a relative humidity of 63 to 67%.

VALUE

DESCRIPTION

0306

0508

0612

Capacitance range (E6 series); note 1:

10 V

16 V

25 V

50 V

100 to 220 nF

−

100 to 220 nF

10 to 100 nF

−

10 to 100 nF

Tolerance on capacitance after 1000 hours

D.F., note 1: 10 V

±10%; ±20%

≤ 5%

16 V

≤ 3.5%

25 V and 50 V

≤ 2.5%

Insulation resistance after 1 minute at U_r(DC)

_ins× C ≥ 500 secon ds

Typical capacitance change as a function of temperature

±15%

Ageing

typical 1% per time decade

Resistance to soldering heat

260 °C; 10 seconds

Note

1. Measured at 20 °C, 1 V and 1 kHz, using a four-gauge method.

MGA488 - 1

∆C

(%)

−5

−10

−15

−40

120

T ( C)

Fig.4 Typical capacitance change as a function

of temperature.

2004 May 14 Rev.8

www.yageo.com

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

TESTS AND REQUIREMENTS

Table 3 Test procedures and requirements

IEC

60384-10/

CECC 32 100

CLAUSE

60068-2

TEST

METHOD

TEST

PROCEDURE

REQUIREMENTS

4.4

mounting

the capacitors may be

mounted on printed-

no visible damage

circuit boards or ceramic

substrates by applying

wave soldering, reflow

soldering (including

vapour phase soldering)

or conductive adhesive

4.5

visual inspection and any applicable method

in accordance with specification

dimension check

using ×10 magnification

4.6.1

4.6.2

capacitance

f = 1 kHz; measuring

voltage 1 V_rmsat 20 °C

measured 1000 hours after date

of manufacture

D.F.

f = 1 kHz; measuring

in accordance with specification

voltage 1 V_rmsat 20 °C

at U_r(DC) for 1 minute

4.6.3

4.6.4

4.7.1

insulation resistance

voltage proof

in accordance with specification

no breakdown or flashover

2.5 × U_rfor 1 minute

temperature

characteristic

between minimum and

maximum temperature

in accordance with specification

4.8

adhesion

a force of 5 N applied for

10 s to the line joining the

terminations and in a

plane parallel to the

substrate

no visible damage

4.9

bond strength of

plating on end face

mounted in accordance

with CECC 32 100,

paragraph 4.4

no visible damage

conditions: bending

1 mm at a rate of 1 mm/s,

radius jig 340 mm

l∆C/Cl: ±10% l

4.10

resistance to

soldering heat

precondition:

120 to 150 °C

the terminations shall be well

tinned after recovery

for 1 minute

260 ±5 °C for 10 ±0.5 s

in a static solder bath

resistance to

leaching

260 ±5 °C for 30 ±1 s

in a static solder bath

using visual enlargement of ×10,

dissolution of the terminations

shall not exceed 10%

2004 May 14 Rev.8

www.yageo.com

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

IEC

60384-10/

CECC 32 100

CLAUSE

60068-2

TEST

METHOD

TEST

PROCEDURE

REQUIREMENTS

4.11

solderability

zero hour test, and test after the terminations shall be well

storage (20 to 24 months) in tinned

original packing in normal

atmosphere;

unmounted chips

completely immersed for

2 ±0.5 s in a solder bath at

235 ±5 °C

4.12

4.14

rapid change of

temperature

preconditioning:

5 cycles in the following

sequence:

30 minutes at −55 °C,

change within 30 minutes to

+125 °C

no visible damage after 24 hours

recovery:

l∆C/Cl: ±15%

damp heat

endurance

preconditioning:

(thermal treatment)

56 days; 40 °C;

no visual damage

after 24 hours recovery:

l∆C/Cl: ±15%

D.F.: ≤7%

90 to 95% RH; U_rapplied

_ins: 1,000 MΩ or R_iC_R≥ 25 s,

whichever is less

after 24 hours recovery:

l∆C/Cl: ±20%

4.15

preconditioning:

(thermal treatment)

1,000 hours at 125 °C and

2 × U_rapplied

D.F.: ≤7%

_ins: 2,000 MΩ or R_iC_R≥ 50 s,

whichever is less

2004 May 14 Rev.8

www.yageo.com

Phycomp

Product specification

Surface-mount ceramic

multilayer capacitors

Low-inductance: Class 2, X7R

10/16/25/50 V

REVISION HISTORY

Revision

Date

Change

Description

Notification

Rev. 5

Rev. 6

Rev. 7

Rev. 8

2001 May 30

2003 Feb 10

2003 Jun 03

2004 May 14

- Converted to Phycomp brand

- Updated company logo

- Size 0306 10 V extended

2004 May 14 Rev.8

www.yageo.com

225506015637 [YAGEO]

相关型号：

225506015649

225506055638

225507155641

225507155643

225507155644

225507155645

225507155646

225507155647

225507155648

225507155649

225508155654

225510615649