PolyFlexTM
Technical Data Sheet
PolyFlexTM is a highly flexible yet easy to print 3D printing material. Featuring good elasticity and a large strain-to-
failure, PolyFlexTM opens up a completely new realm of applications.
Physical Properties
Property
Testing Method
Typical Value
1.17 - 1.24
ASTM D792
(ISO 1183, GB/T 1033)
Density (g/cm3 at 21.5 °C)
Glass transition temperature (°C)
DSC, 10 °C/min
Not available
Not available
Softening temperature of filament
(for 1.75 mm; °C)
Custom method
Melt index (g/10 min)
Moisture content1 (%)
Odor
210 °C, 1.2 kg
10 - 12
≤ 0.1%
Thermogravimetric
/
/
Almost odorless
Insoluble in water
Solubility
Note:
1. For newly opened filaments; filaments may absorb higher levels of moisture during use.
Mechanical Properties1
Property
Testing Method
Typical Value
~ 95A
ASTM D2240
(ISO 7619, GB/T 531)
Shore A hardness
100% modulus (MPa)
Tensile strength (MPa)
Elongation at break (%)
ASTM D412
(ISO 37, GB/T 528)
9.4 ± 0.3
29.0 ± 2.8
ASTM D412
(ISO 37, GB/T 528)
ASTM D412
(ISO 37, GB/T 528)
330.1 ± 14.9
Note:
1. All testing specimens were printed using a MakerBot Replicator 2 under the following conditions:
Printing temperature = 225 °C, printing speed = 90 mm/s, number of shells = 2, and 100% infill.
Global Office Locations
Shanghai ∙ New York ∙ Utrecht ∙ Tokyo
www.polymaker.com
inquiry@polymaker.com
Testing Geometries
115.00
80.00
33.00
Z axis
R25.00
R14.00
Fig 1. Tensile testing specimen
Disclaimer
The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be
used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End-
use performance of printed parts depends not only on materials, but also on part design, environmental conditions, printing
conditions, etc. Product specifications are subject to change without notice.
Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/recycling practices of
Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to
the fitness for any particular use or application. Polymaker shall not be made liable for any damage, injury or loss induced from
the use of Polymaker materials in any particular application.